The role of Sn on microstructure, wear and corrosion properties of Al-5Zn-2.5Mg-1.6Cu-xSn alloy

Résumé

Abstract In the present investigation, Al-5Zn-2.5Mg - 1.6Cu -xSn (x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0 wt%) alloys were fabricated using melting and casting technique. The microstructures of the alloys were studied using optical, scanning electronic microscope/EDS and X-ray diffraction. The corrosion behaviour was performed using electrochemical measurements and immersion tests while the wear behaviour was carried out by pin-on-disc technique. The findings revealed that incorporating Sn to the Al-5Zn-2.5Mg alloy improved its corrosion and wear resistance due to refining the grains. The corrosion potentials shifted from −884 to −943,−955, −996,−1008 and −1012 mV (Ag / AgCl), while the coefficient of friction declined from 0.69 to 0.62 , 0.51 , 0.34, 0.29 and 0.22 with increment of Sn content from 0.0 to 0.2, 0.4. 0.6, 0.8 and 1.0 wt%, respectively. On the other hand, the results illustrated that the wear rate diminished from 4.42 *10−3to 1.47 * 10−3(mm3/Nm) with increasing Sn from 0.0 to 1.0 wt%. Furthermore, the findings showed that increment of Sn content stimulated the uniform corrosion on the surface of alloys.

Citer ce document

Accès au document

Ce document est hébergé sur son dépôt institutionnel d'origine.

Auteur(s)

Statistiques

Consultations : 1

Téléchargements : 0