Synergistic Effect of Zn with Ni on ZSM-5 as Propane Aromatization Catalyst: Effect of Temperature and Feed flowrate

Résumé

Abstract This work shows how propane was catalytically converted to aromatic compounds over Zn-Ni/HZSM-5 to investigate the synergistic role of nickel as zinc stabilizer and promoter in propane aromatization. Co-impregnation method was employed for Zn-Ni/ZSM-5 synthesis fixed 2 wt. % of zinc and 1, 2 and 3 wt. % of nickel. Modified catalysts were fully characterized. Catalysts crystallinity, structure and microporosity were retained from analysis results. Propane aromatization process was conducted at 540 oC, 1200 ml/g-h gas hourly space velocity and atmospheric pressure. The presence of Ni with Zn improved catalytic performance for all Ni loading. Aromatic selectivity and propane conversion were improved with best performance to be Zn-Ni/ZSM-5 with 2 wt. % Zn, 2 wt. % Ni on ZSM-5 averaging 88 and 60 % for twelve hours’ time on stream. Aromatic selectivity on Zn-Ni/ZSM-5 is eight times better than the parent HZSM-5 and one and half times better than the Zn/ZSM-5 catalyst. The electronic interaction of zinc and nickel resulting from equality of oxidation state of +1 and +2 and metal binding energy change synergistically improved the catalytic performance of the bimetallic Zn-Ni/ZSM-5 over the HZSM-5 and Zn/ZSM-5. Flowrate increase from 6 to 35 ml min-1 was found to decrease propane conversion from 80-40 % with increased aromatic selectivity from 55-80 %. Temperature increase from 500-580 oC favours both propane conversion and aromatic selectivity increase from 50-68 and 55-92 % respectively. The metallic interactions from H2-TPR and XPS analysis revealed strong improvement on propane conversion, aromatic selectivity and product distribution.

Citer ce document

Accès au document

Ce document est hébergé sur son dépôt institutionnel d'origine.

Auteur(s)

Statistiques

Consultations : 1

Téléchargements : 0