Variation of the Hydraulic Conductivity and the Mechanical Characteristics of Plastic Concrete with Time
Résumé
Abstract Sand-bentonite-cement are commonly used as cut-off walls to isolate polluted soils or in ground improvement technologies and as retaining structures as secant pile wall. In this research, a laboratory program consisted from 105 sample were prepared and tested between different tests, such as hydraulic conductivity, porosity, and compressive strength to monitor the mechanical behavior of sand-bentonite-cement at different ages. Based on the experimental relationships between hydraulic conductivity coefficient and samples age; there were reduction due to added bentonite to mixture reach about 35.0% at 7 days. Moreover, the average reduction in the compressive strength of plastic concrete samples with bentonite was lower by average range about 51.0% than the compressive strength of plastic concrete samples without bentonite at 7 days. In this study, proposed formulas were derived to estimate the splitting tensile strength based on the compressive strength and the hydraulic conductivity in terms of the bentonite/cement ratio and testing age. The predicted values showed well agreement with the experimental records for samples of sand-bentonite-cement mixtures where the standard deviation and coefficient of variation were 0.02, and 0.94%, respectively.
Citer ce document
Accès au document
Texte intégral en lecture en ligne, réservé aux abonnés SPHAERO et aux membres de l'institution. Se connecter
Voir l'article sur le site de la revueAuteur(s)
Statistiques
Consultations : 1
Téléchargements : 0