Boosting brackish water treatment via integration of mesoporous γ-Al2O3NPs with thin-film nanofiltration membranes

Résumé

Abstract In this study, a simple method based on non-ionic surfactant polysorbates-80 was used to create mesoporous γ-Al2O3NPs. The properties of the prepared mesoporous alumina nanoparticles (Al2O3NPs) were verified using ATR-FTIR, XRD, SEM, TEM, DLS, and BET surface area analysis. Then, thin-film nanocomposite (TFN) nanofiltration membranes were fabricated by interfacial polymerization of embedded polyamide layers with varied contents (0.01 to 0.15 wt.%) of mesoporous γ-Al2O3NPs. The surface roughness, porosity, pore size, and contact angle parameters of all the prepared membranes were also determined. The performance of the fabricated membranes was investigated under various mesoporous γ-Al2O3NPs loads, time, and pressure conditions. Mesoporous γ-Al2O3NPs revealed an important role in raising both the membrane hydrophilicity and the surface negativity. The addition of 0.03 wt.% mesoporous γ-Al2O3NPs to the TFN membrane increased water flux threefold compared to the TF control (TFC) membrane, with maximum water flux reaching 96.5, 98, 60, and 52 L/(m2.h) for MgSO4, MgCl2, Na2SO4, and NaCl influent solutions, respectively, with the highest salt rejection of 96.5%, 92.2%, 98.4%. The TFN-Al2O3 membrane was also able to soften water and remove polyvalent cations such as Mg2+with a highly permeable flux. The TFN-Al2O3membrane successfully removed the hardness of the applied water samples below the WHO limit compared to using merely the TFC membrane. Furthermore, the TFN-Al2O3nanofiltration membrane unit proved to be a promising candidate for the desalination of real brine like that collected from the Safaga area, Egypt.

Citer ce document

Accès au document

Ce document est hébergé sur son dépôt institutionnel d'origine.

Auteur(s)

Statistiques

Consultations : 1

Téléchargements : 0