Evaluation of compressive strength, microhardness and solubility of zinc-oxide eugenol cement reinforced with E-glass fibers
Résumé
BACKGROUND: Zinc-oxide eugenol (ZOE) cements are among the most used temporary materials in dentistry. Although ZOE has advantages over other temporary fillers, its mechanical strength is weaker, so researchers are working to improve it. E-glass fibers have emerged as promising reinforcing fibers in recent years due to their strong mechanical behavior, adequate bonding, and acceptable aesthetics. OBJECTIVES: To evaluate and compare the compressive strength, surface microhardness, and solubility of the ZOE and those reinforced with 10 wt.% E-glass fibers. METHODS: A total of 60 ZEO specimens were prepared; 30 specimens were reinforced with 10 wt.% E-glass fibers, considered modified ZOE. The characterization of the E-glass fibers was performed by XRF, SEM, and PSD. The compressive strength, surface microhardness, and solubility were evaluated. Independent sample t-tests were used to statistically assess the data and compare mean values (P ≤ 0.05). RESULTS: The results revealed that the modified ZOE showed a significantly higher mean value of compressive strength and surface microhardness while having a significantly lower mean value of solubility compared to unmodified ZOE (P ≤ 0.05). CONCLUSION: The modified ZOE with 10 wt.% E-glass fibers had the opportunity to be used as permanent filling materials.
Citer ce document
Accès au document
Texte intégral en lecture en ligne, réservé aux abonnés SPHAERO et aux membres de l'institution. Se connecter
Voir l'article sur le site de la revueAuteur(s)
Statistiques
Consultations : 1
Téléchargements : 0