Structural and Surface Modifications by Varying Precursor Concentrations on Spray Deposition of Zno Thin Films

Résumé

Abstract Zinc Oxide thin films have been deposited on glass substrates using zinc acetate as starting precursor at different concentrations 0.05–0.3 M in steps of 0.05 M by spray pyrolysis method at the constant substrate temperature of 350º C. Lattice structure of the prepared ZnO films were characterized by X-Ray diffraction analysis (XRD). Diffraction pattern revealed hexagonal wurtzite structure with cell edges a = 3.2530 Å, c = 5.2092 Å and density 5.66 g/cm3, which is almost equal to the standard values a = 3.2556 Å, c = 5.2070 Å and 5.6525 g/cm3 (COD No: 96-900-4180). Structural parameters such as dislocation density, lattice stress, unit cell volume, number of crystallites per unit area have been calculated and its dependency with thickness was studied. As the film thickness increases, the crystallite size also increases. Through FTIR, chemical bonds and their stretching vibrations confirmed the metal-oxide phase formation. Scanning electron microscope images showed the formation of good quality film with regularly distributed spherical shaped grains. Roughness values of the films were attained from the Atomic force microscope images. In overall observations, precursor concentration has significant effect on film thickness which in turn modified the structural, optical and morphology properties of the prepared ZnO thin films.

Citer ce document

Accès au document

Ce document est hébergé sur son dépôt institutionnel d'origine.

Auteur(s)

Statistiques

Consultations : 1

Téléchargements : 0