Is There a Correlation Between Physical Properties and Film Thickness of Dual- and Photo- polymerized Luting Resins and CAD/CAM-Dentin Micro-Tensile Bond Strength?

Article scientifique 2024 Anglais

Résumé

Abstract Objective To correlate µTBS of photo- and dual-polymerized luting resins with film thickness (FT), Vicker's hardness (HV) and ultimate-tensile strength (UTS).Methods Human molars (N = 30) were divided (6-groups) according to: 1: Luting resin: Dual- [Bifix QM, (BF)], or photo-polymerized [GrandioSo Heavy Flow (GHF) and VisCalor Bulk (VB)] and 2: Adhesive mode (Optibond Universal): Etch-and-rinse (ER) or self-etching (SE). CAD/CAM blocks (7x7x4mm3) were air-abraded (50µm Al2O3/10s/0.2MPa) and silanated. For ER, dentin was etched (15s), rinsed (30s), and blot-dried. For both modes, adhesive was applied (20s), air-dried (5s) and photo-polymerized (10s). Sticks (1x1mm2) were aged either for 24-hours or for 6-months. Sticks were pulled in tension (1mm/min). Debonded sticks were evaluated for failure mode. For FT, nine-bonded slabs/each cement were evaluated. For UTS, eight-hourglass specimens/each cement were tested. For HV, 5-discs/each cement were evaluated using Vicker’s hardness tester. Data were analysed using ANOVA/Pearson's correlation tests (α = 0.05).Results No correlation between µTBS/HV was revealed (P > 0.05). Positive correlation between µTBS/FT and µTBS/UTS (p < 0.05) were observed. Three-Way ANOVA revealed all experimental factors had significant effect on µTBS (p < 0.05). The VB showed significant lower µTBS (20.8 ± 9.3MPa). The ER mode showed higher µTBS (26.0 ± 10.9MPa), and 24-hours revealed the higher µTBS (27.4 ± 10.0MPa). Mixed failure was the predominate type (42.51%). The VB showed the highest FT (122.2 ± 11.9µm). The GHF revealed higher UTS and HV (112.5 ± 19.7MPa and 91.6 ± 0.4Kgf respectively).Conclusions Photo-polymerized flowable resin can substitute dual-polymerized cement for CAD/CAM composite bonding.Clinical relevance: Photo-polymerized flowable composite can replace the dual-polymerized resin cement one to bond CAD/CAM composite to dentin.

Citer ce document

El-Askary, F., Tadros, N., Hassanien, A., Aboalazm, E., Kamel, M., Özcan, M. (2024). Is There a Correlation Between Physical Properties and Film Thickness of Dual- and Photo- polymerized Luting Resins and CAD/CAM-Dentin Micro-Tensile Bond Strength?. https://doi.org/10.21203/rs.3.rs-3903230/v1

Accès au document

Texte intégral en lecture en ligne, réservé aux abonnés SPHAERO et aux membres de l'institution. Se connecter

Voir l'article sur le site de la revue

Auteur(s)

Farid Sabry El-Askary Nader Tadros Abdullah Hassanien Emad Aboalazm M.A. Kamel Mutlu Özcan

Statistiques

Consultations : 1

Téléchargements : 0