Structural and Electronic Properties of Cu2+ Doped LiMn2O4 Cathode Material for Rechargeable Lithium Ion Battery: A DFT Study

Résumé

Spinel LiMn2O4 offers a potentially attractive alternative to the commercialized LiCoO2 because of its low cost, non-toxicity, good rate performance and superior safety, but experiences severe capacity fading as a result of Jahn-Teller cubic phase transition to unstable tetragonal phase especially when operated at elevated temperature (>55oC). Among the various techniques carried out to overcome these setbacks is doping with cations to raise the oxidation state of Mn thereby decreasing the amount of unstable Mn3+. This study focuses on the investigation of the structural and electronic properties of Cu2+ doped LiMn2O4 using ab-initio computational method. The structural properties of both un-doped LiMn2O4 and Cu2+ doped LiMn2O4 were collectively obtained using both generalized gradient approximation (GGA) employing pseudo-potentials, plane wave basis sets and XcryDen. From the electronic properties of undoped LiMn2O4, it was revealed that in LiMn2O4, only Mn3+ ions contribute to conduction, even though Mn3+ ions and Mn4+ ions exist together. Increasing the number of Mn3+ brings it a unique challenge of instability. Due to this instability, avoiding the Mn3+ state of manganese prevents Jahn-teller distortion, resulting in a reduced phase transition. Based on the results from the first-principles calculation of Cu2+ doped LiMn2O4, the Cu valence in doped spinel LiCu0.25Mn0.75O4 is Cu2+ at a fully lithiated state. When half of the Li ions are extracted, the Cu2+ ions oxidized to Cu3+ ions. Since Cu2+ is a di-valent element, the dopant act as electrochemically active centres for valence change, leaving two trivalent ions to only take on +4 oxidation states stably, thus increasing Mn-O bonding strength which ultimately suppressed Jahn-Teller distortions. However, previous studies show that Cu2+ substitution shrinks the lattice because the ionic radius of Cu2+ is smaller than that of the host Mn3+ ions, thereby the reversible capacity of Cu-doped spinel may be reduced as Cu ions can only provide one electron per ion.

Citer ce document

Accès au document

Ce document est hébergé sur son dépôt institutionnel d'origine.

Auteur(s)

Statistiques

Consultations : 1

Téléchargements : 0