Morphological and magnetic features of Ru(III) doped magnetite ultrafine nanoparticles

Résumé

Abstract Magnetite nanoparticles constitute a class of nanoparticles which is easily manipulated using a magnetic field. Magnetite nanoparticles doped with ruthenium (Ru) ions [RuxFe(3−x)O4] were synthesized via co-precipitation method where 0.0 ≤ x ≤ 0.5 with step 0.1. The obtained nanopowder was investigated via x-ray diffraction, FTIR, FESEM. It was shown that Ru ions were incorporated successfully into a magnetite structure with a slight influence on the value of the lattice parameter which increased from 8.354 Å at x = 0.0 to be 8.403 Å at x = 0.3, while crystallite size deteriorated from 20.1 nm at x = 0.0 to be around 3 nm at x = 0.3. In addition, the surface roughness average was influenced by the dopant content, where it decreased from 35.6 nm at the pure magnetite to be 25.87 nm at x = 0.3. The ICP examination indicated that the measured contents of Ru ions through competitions were around 41 ppm and increased to 190 ppm comparing with 43 and 199 ppm as a theoretical value both x = 0.1 and 0.5. Regarding magnetic properties, the coercivity raised from 40.11 Oe and raised 44.66 Oe for x = 0.0 and 0.5, respectively. This manipulated behavior of magnetite due to dopant suggests that desired properties could be achieved via the dopant strategy to be used for several applications.

Citer ce document

Accès au document

Ce document est hébergé sur son dépôt institutionnel d'origine.

Auteur(s)

Statistiques

Consultations : 1

Téléchargements : 0