The electrochemical corrosion behaviour of compacted (Bi, Pb)-2223 superconductors in aqueous solutions

Résumé

The corrosion behaviour of (Bi, Pb)-2223 samples compacted at 0.3-1.9 GPa in 0.5 M of HCl, NaCl, and NaOH solutions at 30 °C was investigated using potentiodynamic polarization curves measurements and electrochemical impedance spectroscopy (EIS) technique as well as scanning electron microscopy (SEM) and energy dispersive X-ray emission spectroscopy (EDX). Polarization results showed that the increase in compaction decreases both cathodic hydrogen evolution or oxygen reduction and anodic (BiPb)-2223 superconductor dissolution in 0.5 M HCl, and 0.5 M NaOH. On the other hand, compaction mainly affects the anodic part of the polarization curves of (Bi, Pb)-2223 in 0.5 M NaCl solution. EIS measurements revealed that the highest protection of the superconductors was achieved in 0.5 M NaCl, while the lowest degree of protection was observed in 0.5 M HCl. SEM images show a random plate-like morphology fitted with the marker of (Bi, Pb)-2223 material. The compacted sample at 1.9 GPa indicates deformation of the grains and the formation of a micro-crack. The corrosion mechanism of the superconductor at different pH values was also discussed.

Citer ce document

Accès au document

Ce document est hébergé sur son dépôt institutionnel d'origine.

Auteur(s)

Statistiques

Consultations : 1

Téléchargements : 0